Nonlinear optical crystal AGSe (AgGaSe2) |
|
| (silver gallium selenide) |
|
| Main properties |
|
| Negative uniaxial crystal |
no > ne (at l < 0.804 µm ne > no) |
| Transparency range, µm |
0.71 - 18 |
| Nonlinear coefficient, pm/V |
d36 = 33 |
| Symmetry |
Tetragonal, -42m point group |
| Cell parameters, Å |
a=5.9921, c=10.883 |
Typical Reflection index |
10.6 µm 5.3 µm |
no=2.5915, ne=2.5582 no=2.6138, ne=2.5811 |
Optical Damage Threshold, MW/cm2 |
1064 nm (t=10 ns) |
350 |
| Walk off angle, ° |
5.3 µm |
0.68 |
| Thermal conductivity k, WM/M°C |
1.1 |
| Band-gap energy at room temperature, eV |
Eg = 1.83 |
| Optical activity ρ = 522deg/mm at isotropic point, µm |
no = ne, l = 0.804 |
|
|
| The parameters of optical elements |
|
| Orientation accuracy, arc min |
< 30 |
| Parallelism, arc sec |
< 40 |
| Flatness |
546 nm |
l/4 |
| Surface quality, scratch/dig |
30/20 |
|
|
| Application |
|
- Efficient frequency doubling for mid-IR radiation.
- Optical parametric oscilation and amplification, Different frequency generation to mid-infrared regions up to 17 µm
- Optical narrow-band filters in the region near isotropical point (0.804 µm at 300 K)
|
|
We are able to provide suitable Anti-reflection / Protective, etc. coatings tailored to customer's specifications, reflectivity curves are applied upon request. |
|
|
|